From: Rational design of nonstoichiometric bioceramic scaffolds via digital light processing: tuning chemical composition and pore geometry evaluation

Fig. 3

Apparent compressive strength (a) and Young’s modulus (b) of the CSi-Mg5Srx scaffolds after sintering at 1150 °C. Specific compressive strength and Young’s modulus on apparent density (c, d) and minimal cross-sectional area (e, f) respectively of the bioceramic scaffolds after sintering. * p < 0.05